Pure Nickel Wire price 0.25mm Ni201 Ni200 for wire mesh

• Application: Aviation, Electronics, Industrial, Medical, Chemical
• Standard: JIS, GB, DIN, ASTM
• Purity: >99.5%
• Alloy: Non-alloy
• Type: Nickel Wire
• Powder: Not Powder
• Model NO.: nickel 200
• sample: free
• Surface: Bright
• Condition: Soft 1/4H 1/2H Hard
• Elongation: 35%
• Density: 8.89g/cm3
• melting point: 1440C
• Name: N02201
• Shape: Strip/Ribbon/Wire
• Spool: DIN 250 DIN200
• Transport Package: Strand Packing
• Specification: 0.25
• Trademark: TANKII
• Origin: Shanghai
• HS Code: 7506100000
• Production Capacity: 2000Tons/year

Product Description

Pure Nickel Wire price 0.25mm Ni201 Ni200 for wire mesh

Nickel 201 is a low carbon variety compared with Nickel 200, possessing low annealed hardness and a very low work-hardening rate, desirable for cold forming operations. It is highly resistant to corrosion by neutral and alkaline salt solutions, fluorine and chlorine, but in oxidising salt solutions severe attack will occur.
The applications of pure nickel includes food and synthetic fiber processing equipment, electronic parts, aerospace and missile components, handling of sodium hydroxide above 300ºC.
Chemical Composition

Grade	Element Composition/%
	Ni+Co	Mn	Cu	Fe	C	Si	Cr	S
Ni201	≥99.0	≤0.35	≤0.25	≤0.30	≤0.02	≤0.3	≤0.2	≤0.01
Ni200	≥99.0	/≤0.35	≤0.25	≤0.30	≤0.15	≤0.3	≤0.2	≤0.01

Physical Data

Density	8.9g/cm3
Specific Heat	0.109(456 J/kg.ºC)
Electrical Resistivity	0.085×10-6ohm.m
Melting Point	1435-1445ºC
Thermal Conductivity	79.3 W/m-K
Mean Coeff Thermal Expansion	13.1×10-6m/m.ºC

Typical Mechanical Properties
 

Mechanical Properties	Nickel 201
Tensile Strength	403 Mpa
Yield Strength	103 Mpa
Elongation	50%

Our Production Standard
 

	Bar	Forging	Pipe	Sheet/Strip	Wire
ASTM	ASTM B160	ASTM B564	ASTM B161/B163/B725/B751	AMS B162	ASTM B166

 

Diameter(mm)	Tolerance(mm)	Diameter(mm)	Tolerance(mm)
0.03-0.05	±0.005	>0.50-1.00	±0.02
>0.05-0.10	±0.006	>1.00-3.00	±0.03
>0.10-0.20	±0.008	>3.00-6.00	±0.04
>0.20-0.30	±0.010	>6.00-8.00	±0.05
>0.30-0.50	±0.015	>8.00-12.0	±0.4