• Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)
  • Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)
  • Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)
  • Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)
  • Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)

Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)

Certification: RoHS, ISO9001, ASTM, JIS, GB
Surface Treatment: Enameled Wire
Alloy: Alloy
standard: GB/ASTM/JIS/BIS/DIN
surface: bright
Sample: Free
Customization:

Contact Supplier

Diamond Member Since 2008

Suppliers with verified business licenses

Basic Info.

Model NO.
6J12
Classification
Precious Metal
Serves
Small Order Accepted
Transport Package
According to Client′s Requirement
Specification
0.01-10mm
Trademark
TANKII
Origin
China
HS Code
7409900000
Production Capacity
2000tons/Year

Product Description

Manganin Wire/ Shunt Resistor (6J13, 6J12, 6J8)

Product Description

 Manganin wire widely used for low voltage instrumentation with the highest requirements, the resistors should be carefully stabilised and the application temperature should not exceed +60 °C. Exceeding the maximum working temperature in air may result in a resistance drift generated by oxidizing. Thus, the long-term stability can be affected negatively.  As a result, the resistivity as well as the temperature coefficient of  the electric resistance may slightly change. It is also used as low cost replacement material for silver solder for hard metal mounting.

Chemical Content, %

Ni

Mn

Fe

Si

Cu

Other

ROHS Directive

Cd

Pb

Hg

Cr

2~5

11~13

<0.5

micro

Bal

-

ND

ND

ND

ND

Mechanical Properties

Max Continuous Service Temp

0-100ºC

Resisivity at 20ºC

0.44±0.04ohm mm2/m

Density

8.4 g/cm3

Thermal Conductivity

40 KJ/m·h·ºC

Temp Coefficient of Resistance at 20 ºC

0~40α×10-6/ºC

Melting Point

1450ºC

Tensile Strength(Hard)

585 Mpa(min)

Tensile Strength,N/mm2   Annealed,Soft

390-535

Elongation

6~15%

EMF vs Cu, μV/ºC (0~100ºC)

2(max)

Micrographic Structure

austenite

Magnetic Property

non

Hardness

200-260HB

Micrographic Structure

Ferrite

Magnetic Property

Magnetic

Manganin Applications:  

1;  It is used for making wire wound precision resistance

2;  Resistance boxes

3; Shunts for electrical measuring instruments

Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)
Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)
Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)
Manganin Wire for Shunt Resistor (6J13, 6J12, 6J8)

 

Send your message to this supplier

*From:
*To:
avatar Mr. Martin
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now