TK 1 Fe-Cr-Al alloy wire rod 0.5mmd
TK 1 (Kan A1 ) large-sized cold-drawn wire products can be used for high-temperature resistance furnace.
Practice has proved that: the product process is stable, integrated performance is good. Has good high temperature oxidation
resistance and longer service life; excellent winding properties at room temperature processing, ease of
processing molding; little rebound resilience and so on. Processing performance is very good; operating
temperature can reach 1400 deg .
Conventional Product specifications: 0.5 ~ 10 mm
| Properties \ Grade |
Kan-thal A1 | |||
| Cr | Al | Re | Fe | |
| 20.5--23.5 | 5.8 | Suitable | Balance | |
| Max Continuous ServiceTemperature(ºC) |
Diameter 1.0-3.0 | Diameter large than 3.0, | ||
| 1225-1350ºC | 1400ºC | |||
| Resisivity 20ºC (Omm2/m) | 1.45 | |||
| Density(g/cm 3 ) | 7.1 | |||
| Approximate Melting Point( ºC) | 1520 | |||
| Elongation (%) | 16-33 | |||
| Repeatedly Bend Frequency(F/R)20ºC | 7-12 | |||
| Continuous Service Time under 1350ºC | More than 60 hours | |||
| Micrographic Structure | Ferrite | |||
The relationship between the maximum operating temperature and the furnace atmosphere
| Furnace atmosphere | Dry Air | Humid Air | hydrogen-argon gas | Argon | Decomposition ammonia gas |
| Temp( ºC) | 1400 | 1200 | 1400 | 950 | 1200 |