| Customization: | Available |
|---|---|
| Product Type: | Wire |
| Material: | FeCrAl |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Cr | Si | Mn | Cr | Al | Fe | |
| Nominal composition | Bal. | |||||
| Min(%) | 20.5 | 5.3 | ||||
| Max(%) | 0.080 | 0.7 | 0.4 | 23.5 | 6.3 |
| Wire Size | Yield Strength | Tensile Strength | Elongation |
| diameter | Rp0.2 | Rm | A |
| mm | MPa | MPa | % |
| 1.6 | 830 | 930 | 5 |
| Deposit Efficiency(%) | 62-78 |
| Hardness HV (300g) | 165-280 |
| Surface roughness(um) | 11-16 |
| Porosity(%) | 1-6* |
| Oxides(%) | 5-20* |
| Product name | Size range |
| Cold drawing wire | Diameter 0.03-7.5mm |
| Hot-rolled wire rod | Diameter 8.0-12mm |
| Ribbon | Thickness 0.05-0.35mm |
| Width 0.5.0-3.5mm | |
| Cold rolled strip | Thickness 0.5-2.5mm |
| Width 5.0-40mm | |
| hot rolled strip | Thickness 4-6mm |
| Width 15-40mm |
| basic parameters | APMTM | FeCrAl | ||
| A-1 | AF | D | ||
| The highestcontinuous working temperature | 1425 | 1400 | 1300 | 1300 |
| The nominal chemical composition,% Cr | 22 | 22 | 22 | 22 |
| AI | 5.8 | 5.8 | 5.3 | 4.8 |
| Fe | ingredients | ingredients | ingredients | ingredients |
| Ni | - | - | - | - |
| The resistivity in 20ºC,Ωmm-2mm-1 | 1.45 | 1.45 | 1.39 | 1.35 |
| density,g/cm3 | 7.1 | 7.1 | 7.15 | 7.25 |
| Thermal expansion coefficientK-1 20-750ºC | 14×10-6 | 14×10-6 | 14×10-6 | 14×10-6 |
| 20-1000ºC | 15×10-6 | 15×10-6 | 15×10-6 | 15×10-6 |
| The thermal conductivity 20ºC,Wm-1K-1 | 13 | 13 | 13 | 13 |
| Specific heat capacity 20ºC,KJkg-1K-1 | 0.46 | 0.46 | 0.46 | 0.46 |
| Melting pointºC | 1500 | 1500 | 1500 | 1500 |
| Probably mechanical characteristics | ||||
| Tensile strength,N mm-2 | 680 | 680 | 680 | 650 |
| The yield strength,N mm-2 | 470 | 475 | 475 | 450 |
| Hardness,Hv | 230 | 230 | 230 | 230 |
| Breaking elongation,% | 20 | 18 | 18 | 18 |
| 900ºCTensile strength,N mm-2 | 40 | 34 | 37 | 34 |
| Creep strength 800ºC | 11 | 6 | 8 | 6 |
| 1000ºC | 3.4 | 1 | 1.5 | 1 |
| Magnetic | magnetic(In the temperature600ºC) | |||
| Emissivity, the oxidation conditions | 0.7 | 0.7 | 0.7 | 0.7 |
| Alloy Type | Diameter | Resistivity | Tensile | Elongation(%) | Bending | Max.Continuous | Working Life |
| (mm) | (μΩm)(20°C) | Strength | Times | Service | (hours) | ||
| (N/mm²) | Temperature(°C) | ||||||
| Cr20Ni80 | <0.50 | 1.09±0.05 | 850-950 | >20 | >9 | 1200 | >20000 |
| 0.50-3.0 | 1.13±0.05 | 850-950 | >20 | >9 | 1200 | >20000 | |
| >3.0 | 1.14±0.05 | 850-950 | >20 | >9 | 1200 | >20000 | |
| Cr30Ni70 | <0.50 | 1.18±0.05 | 850-950 | >20 | >9 | 1250 | >20000 |
| ≥0.50 | 1.20±0.05 | 850-950 | >20 | >9 | 1250 | >20000 | |
| Cr15Ni60 | <0.50 | 1.12±0.05 | 850-950 | >20 | >9 | 1125 | >20000 |
| ≥0.50 | 1.15±0.05 | 850-950 | >20 | >9 | 1125 | >20000 | |
| Cr20Ni35 | <0.50 | 1.04±0.05 | 850-950 | >20 | >9 | 1100 | >18000 |
| ≥0.50 | 1.06±0.05 | 850-950 | >20 | >9 | 1100 | >18000 | |
| 1Cr13Al4 | 0.03-12.0 | 1.25±0.08 | 588-735 | >16 | >6 | 950 | >10000 |
| 0Cr15Al5 | 1.25±0.08 | 588-735 | >16 | >6 | 1000 | >10000 | |
| 0Cr25Al5 | 1.42±0.07 | 634-784 | >12 | >5 | 1300 | >8000 | |
| 0Cr23Al5 | 1.35±0.06 | 634-784 | >12 | >5 | 1250 | >8000 | |
| 0Cr21Al6 | 1.42±0.07 | 634-784 | >12 | >5 | 1300 | >8000 | |
| 1Cr20Al3 | 1.23±0.06 | 634-784 | >12 | >5 | 1100 | >8000 | |
| 0Cr21Al6Nb | 1.45±0.07 | 634-784 | >12 | >5 | 1350 | >8000 | |
| 0Cr27Al7Mo2 | 0.03-12.0 | 1.53±0.07 | 686-784 | >12 | >5 | 1400 | >8000 |
){kind=link}