Monel 400, Alloy 400; Nickel 400; Nickelvac 400 Tube/Pipe

• Customization: Available
• Product Type: Strip
• Material: copper alloy
• Model NO.: Alloy 400
• Carbon Content: 0
• PCD: 290min
• ET: 0
• Hole: 0
• standard: GB/ASTM/JIS/BIS/DIN
• Size: 0.01-3mm*0.3-600mm
• surface: bright
• Sample: Small Order Accepted
• Transport Package: in Roll/Coil/Spool
• Specification: 0.01-3mm*0.3-600mm
• Trademark: Tankii
• Origin: Shanghai, China
• HS Code: 7409400000
• Production Capacity: 2000tons/Year

Product Description

Monel 400, Alloy 400; Nickel 400; Nickelvac 400 Tube/Pipe

General Description
Monel 400(UNS N04400/2.4360) is a nickel-copper alloy with high strength and excellent resistance to a range of media including seawater, dilute hydrofluoric and sulfuric acids, and alkalies.
Monel 400 containing about 30-33% copper in a nickel matrix has many similar characteristics of commercially pure nickel, while improving upon many others. Addition of some iron significantly improves the resistance to cavitation and erosion in condenser tube applications. The main uses of Monel 400 are under conditions of high flow velocity and erosion as in propeller shafts, propellers, pump-impeller blades, casings, condenser tubes, and heat exchanger tubes. Corrosion rate in moving seawater is generally less than 0.025 mm/year. The alloy can pit in stagnant seawater, however, the rate of attack is considerably less than in commercially pure alloy 200. Due to its high nickel content (approx. 65%) the alloy is generally immune to chloride stress corrosion cracking. The general corrosion resistance of Monel 400 in nonoxidizing mineral acids is better compared to nickel. However, it suffers from the same weakness of exhibiting very poor corrosion resistance to oxidizing media such as nitrica acid, ferric chloride, cupric chloride, wet chlorine, chromic acid, sulfur dioxide, or ammonia. In unaerated dilute hydrochloric and sulfuric acid solution the alloy has useful resistance up to concentrations of 15% at room temperature and up to 2% at somewhat higher temperature, not exceeding 50°C. Due to this specific characteristic, Monel 400 produced by NiWire is also used in processes where chlorinated solvents may form hydrochloric acid due to hydrolysis, which would cause failure in standard stainless steel.

Monel 400 possesses good corrosion resistance at ambient temperatures to all HF concentration in the absence of air. Aerated solutions and higher temperature increase the corrosion rate. The alloy is susceptible to stress corrosion cracking in moist aerated hydrofluoric or hydrofluorosilic acid vapor. This can be minimized by deaeration of the environments or by stress relieving anneal of the component in question.

Typical applications are valve and pump parts, propeller shafts, marine fixtures and fasteners, electronic components, chemical processing equipment, gasoline and freshwater tanks, petroleum processing equipment, boiler feedwater heaters and other heat exchangers
Chemical Composition

Grade	Ni%	Cu%	Fe%	C%	Mn%	C%	Mn%	Si%	S%
Monel 400	Min 63	28-34	Max 2.5	Max 0.3	Max 2.0	Max 0.05	Max 1.0	Max 0.5	Max 0.024

Specifications

Grade	UNS	Werkstoff Nr.
Monel 400	N04400	2.4360

Physical Properties

Grade	Density	Melting Point
Monel 400	8.83 g/cm3	1300°C-1390°C

Mechanical Properties

Alloy	Tensile Strength	Yield Strength	Elongation
Monel 400	480 N/mm²	170 N/mm²	35%

Our Production Standard

Standard	Bar	Forging	Pipe/Tube	Sheet/Strip	Wire	Fittings
ASTM	ASTM B164	ASTM B564	ASTM B165/730	ASTM B127	ASTM B164	ASTM B366

Size Range
Monel 400 wire, bar, rod, strip, forging, plate, sheet, tube, fastener and other standard forms are available.