TANKII China factor Stainless Steel Wire 304 SS /Ta-fa 80T welding wire

• Product Type: Wire
• Material: FeCr
• Carbon Content: Low Carbon
• PCD: HRB 95-100
• ET: 0
• Hole: 0
• Model NO.: 304 SS
• Typical Hardnedd: HRB 95-100
• Bond Strength: 4650 psi
• Deposit Rate: 10 lbs/hr/100A
• Deposit Efficiency: 75%
• Transport Package: 15kg/Spool, Carton, Wooden Case
• Specification: 1/16′′, 1.6mm
• Trademark: TANKII
• Origin: Shanghai, China
• HS Code: 75052200
• Production Capacity: 5000 Tons/Year

Product Description

Stainless Steel Wire 304 SS Thermal Spray Wire

Product Introduction:
304 stainless steel wire sprcifically designed for arc spraying. It produces a dense, well-bonded coating with excellent machinability and wear and corrosion resistance. 304 stainless steel is widely used for machine element repair, dimensional restoration and wear resistance applications. It has relatively high shrink characteristics and should not be used for coatings over 0.075 inches thick.
 
Surface Preparation:
Surface should be clean, white metal, with no oxides(rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning.
Recommended methodof preparation is to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
 
Chemical Compositin:

Cr	Ni	Mn	Si	Fe
19.0	9.3	2.0	1.0	Bal.

Typical Characteristics:

Typical Hardness	HRB 95-100
Bond Strength	4650 psi
Deposit Rate	10 lbs/hr/100A
Deposit Efficiency	75%