FeCrAl Alloy Grade | Chemical Composition % | |||||||||
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Re | Others |
max(≤) | ||||||||||
1Cr13Al4 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 12.5-15.0 | ---- | 3.5-4.5 | 0.1 | Bal. |
0Cr15Al5 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 14.5-15.5 | ---- | 4.5-5.3 | 0.1 | Bal. |
0Cr25Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 23.0-26.0 | ≤0.60 | 4.5-6.5 | 0.1 | Bal. |
0Cr23Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 20.5-23.5 | ≤0.60 | 4.2-5.3 | 0.1 | Bal. |
0Cr21Al6 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 19.0-22.0 | ≤0.60 | 5.0-7.0 | 0.1 | Bal. |
0Cr21Al4 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 21.0-23.0 | ≤0.60 | 3.0-5.2 | 0.1 | Bal. |
0Cr21Al6Nb | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.60 | 21.0-23.0 | ≤0.60 | 5.0-7.0 | 0.1 | Bal. |
0Cr27Al7Mo2 | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.40 | 26.5-27.8 | ≤0.60 | 6.0-7.0 | 0.1 | Bal. |
Chemical Composition and Propertes:
Propertes/Grade |
NiCr 80/20 |
NiCr 70/30 |
NiCr 60/15 |
NiCr 35/20 |
NiCr 30/20 |
|
Main Chemical Composition(%) |
Ni |
Bal. |
Bal. |
55.0-61.0 |
34.0-37.0 |
30.0-34.0 |
|
Cr |
20.0-23.0 |
28.0-31.0 |
15.0-18.0 |
18.0-21.0 |
18.0-21.0 |
|
Fe |
≤ 1.0 |
≤ 1.0 |
Bal. |
Bal. |
Bal. |
Max Working Temperature(ºC) |
1200 |
1250 |
1150 |
1100 |
1100 |
|
Resistivity at 20ºC |
1.09 |
1.18 |
1.12 |
1.04 |
1.04 |
|
Density(g/cm3) |
8.4 |
8.1 |
8.2 |
7.9 |
7.9 |
|
Thermal Conductivity (KJ/m· h· ºC) |
60.3 |
45.2 |
45.2 |
43.8 |
43.8 |
|
Coefficient of Thermal Expansion(α × 10-6/ºC) |
18 |
17 |
17 |
19 |
19 |
|
Melting Point(ºC) |
1400 |
1380 |
1390 |
1390 |
1390 |
|
Elongation(%) |
> 20 |
> 20 |
> 20 |
> 20 |
> 20 |
|
Micrographic Structure |
austenite |
austenite |
austenite |
austenite |
austenite |
|
Magnetic Property |
nonmagnetic |
nonmagnetic |
nonmagnetic |
nonmagnetic |
nonmagnetic |
CuNi Alloys Grade | Electrical resistivity (20degreeΩ mm² /m) |
temperature coefficient of resistance (10^6/degree) |
Density g/mm² |
Max. temperature (degree) |
Melting point (degree) |
CuNi1 | 0.03 | < 1000 | 8.9 | 200 | 1085 |
CuNi2 | 0.05 | < 1200 | 8.9 | 200 | 1090 |
CuNi6 | 0.10 | < 600 | 8.9 | 220 | 1095 |
CuNi8 | 0.12 | < 570 | 8.9 | 250 | 1097 |
CuNi10 | 0.15 | < 500 | 8.9 | 250 | 1100 |
CuNi14 | 0.20 | < 380 | 8.9 | 300 | 1115 |
CuNi19 | 0.25 | < 250 | 8.9 | 300 | 1135 |
CuNi22 | 0.30 | < 160 | 8.9 | 300 | 1150 |
CuNi30 | 0.35 | < 100 | 8.9 | 350 | 1170 |
CuNi34 | 0.40 | -0 | 8.9 | 350 | 1180 |
CuNi40 | 0.48 | ± 40 | 8.9 | 400 | 1280 |
CuNi44 | 0.50 | < -6 | 8.9 | 400 | 1280 |