Tankii Manganin Wire/ Strip/ Sheet /Cu86mn12ni2 for Resistor and Shunt 6j12 6j13

• Customization: Available
• Product Type: Strip
• Material: Cumn
• Model NO.: Cu86mn12ni2
• Carbon Content: none
• PCD: none
• ET: none
• Hole: none
• Sample: free
• standard: GB/ASTM/JIS/BIS/DIN
• Serves: Small Order Accepted
• Transport Package: According to Client′s Requirement
• Specification: SGS
• Trademark: TANKII
• Origin: China
• HS Code: 74082200
• Production Capacity: 2000tons/Year

Product Description

Manganin Wire/ Strip/ Sheet /Cu86mn12ni2 for Resistor and Shunt

Product Description
Manganin wire widely used for precision resistors with the highest requirements, the resistors should be carefully stabilised and the application temperature should not exceed +60 °C. Exceeding the maximum working temperature in air may result in a resistance drift generated by oxidizing. Thus, the long-term stability can be affected negatively.  As a result, the resistivity as well as the temperature coefficient of  the electric resistance may slightly change. It is also used as low cost replacement material for silver solder for hard metal mounting.
 
Chemical Content, %

Ni	Mn	Fe	Si	Cu	Other	ROHS Directive
						Cd	Pb	Hg	Cr
2~5	11~13	<0.5	micro	Bal	-	ND	ND	ND	ND

 
Mechanical Properties

Max Continuous Service Temp	0-100ºC
Resisivity at 20ºC	0.44±0.04ohm mm2/m
Density	8.4 g/cm3
Thermal Conductivity	40 KJ/m·h·ºC
Temp Coefficient of Resistance at 20 ºC	0~40α×10-6/ºC
Melting Point	1450ºC
Tensile Strength(Hard)	585 Mpa(min)
Tensile Strength,N/mm2   Annealed,Soft	390-535
Elongation	6~15%
EMF vs Cu, μV/ºC (0~100ºC)	2(max)
Micrographic Structure	austenite
Magnetic Property	non
Hardness	200-260HB
Micrographic Structure	Ferrite
Magnetic Property	Magnetic

 
Resistance Alloy- Manganin Sizes / Temper Capabilities
Condition: Bright, Annealed, Soft 
Wire diameter 0.02mm-1.0mm packing in spool, big than 1.0mm packing in coil
Rod, Bar diameter 1mm-30mm 
Strip: Thickness 0.01mm-7mm, Width 1mm-280mm 
Enameled condition is available