Factory Price Pure Nickel Alloy 200 201 Inconel 600/601/625/718 Welded Seamless Pipe/Tube

• Customization: Available
• Application: Aviation, Electronics, Industrial, Medical, Chemical
• Standard: JIS, GB, DIN, BS, ASTM, AISI
• Model NO.: NI200
• Purity: >99.5%
• Alloy: Non-alloy
• Type: Nickel Pipe
• Powder: Not Powder
• Density: 8.9 g/cm3
• OD: 0.5mm Min
• Wall Thickness: 0.02mm Min.
• Length: 0.5 mm Min.
• Surface: Bright
• sample: accepted small order
• HS: 750711000
• Series: NI 200 NI201 NI212
• other Series: inconel 600 601 625 750 800 etc.
• Product name: NICR alloy, nickel, inconel, precison alloy etc.
• Transport Package: Wooden Case
• Specification: OD: 0.5-200mm
• Trademark: TANKII
• Origin: Shanghai, China
• HS Code: 75052200
• Production Capacity: 500 Tons/Month

Product Description

 

Pure nickel alloy 200 201 inconel 600 601 625 718 weld seamless pipe tube
 

TANKII Alloy 200/201 is extremely resistance to caustic alkalies up to and including the molten state. The extra-low carbon content of Alloy 200/201 gives virtual immunity to intergranular attack above about 315°C. The presence of chlorates must be kept to aminimum, as they accelerate the rate of attack.

Good resistance to corrosion in acids and alkalis and is most useful under reducing conditions.

Application
Alkali industry.
Chlor-alkali chemical and organic chloride production.
Food processing industry.
High temperature halogen and salt corrosion environment.
Electronic instrument parts. Water treatment.
 

 Chemical 

Grade	Ni+Co	Cu	Si	Mn	C	Mg	S	P
N4	99.8	0.015	0.03	0.002	0.01	0.01	0.001	0.001
N6	99.6	0.10	0.10	0.05	0.10	0.10	0.005	0.002
Ni201	≥99.0	≤0.25	≤0.35	≤0.35	≤0.02	/	≤0.01	/
Ni200	≥99.2	≤0.25	≤0.35	≤0.35	≤0.15	/	≤0.01	/

 

Product Parameters

 

Physical Data
Density	Specific Heat	Electrical Resistivity	Melting Point	Thermal Conductivity	Mean Coeff Thermal Expansion
8.89g/cm3	0.109(456 J/kg.ºC)	0.096×10-6ohm.m	1435-1446ºC	70.2 W/m-K	13.3×10-6m/m.ºC
Typical Mechanical Properties
Mechanical Properties	Tensile Strength	Yield Strength	Elongation	Standard
Nickel 200	462 Mpa	148 Mpa	47%	ASTM B161/B163/B725/B751

 Inconel 600:
TANKII Brand Inconel600 alloy is ni - cr - iron base alloy solid solution strengthening, has good resistance to high temperature corrosion and oxidation resistance, good cold and hot machining and welding performance, under 700 ºC has a satisfactory heat intensity and high plasticity.

You can find below Characters of Inconel 600:
(1) has the very good reduction, oxidation resistance, nitride medium corrosion performance;
(2) has good resistance to stress corrosion cracking at noemal and high temperature performance;
(3) has good performance of dry chlorine and hydrogen chloride gas corrosion resistant;
(4) has good mechanical properties at the zero, room and high temperature;
(5) has the very good creep rupture strength, recommended above 700 ° C working environment;

Application Field of Inconel 600:
(1)thermowell in the erosion atmosphere;
(2)vinyl chloride monomer production: corrosion resistance to chlorine, hydrogen chloride, oxidation and carbonization;
(3)uranium oxide into six fluoride: hydrogen corrosion resistance;
(4)the production and usage of caustic alkali metal field, especially the environment of using sulfide;
(5)make titanium dioxide in the way of chlorine;
(6)organic or inorganic chloride and fluoride production: corrosion resistance to chlorine and fluorine;
(7)nuclear reactor;
(8)retort and parts of heat treatment furnace, especially in the carbide and nitride atmosphere;
(9)catalytic regenerator in petrochemical production which in the application of above 700°C is recommended to use  alloy 600 to obtain a longer service life;

Chemical Compositon of Inconel 600 Wt.%:

Inconel 600 (UNS N06600/NS 312)
%	Ni	Cr	Fe			C	Mn	Si			Cu	P	S
Min	72	14	6
Max		17	10			0.15	1	0.5			0.5	0.015	0.015

Inconel 600's Min Value of Mechanical Properties at normal temperature:

Typical        Mechanical Properties	Tensile Srength    Rm N/mm^2	Yield Strength     Rp0.2N/mm^2	Elongation           A5 %	Hardness          HB
annealed treatment	550	240	30	195
solution   treatment	500	180	35	185