High Purity Capillarity Pipe Platinum Iridium Alloy Wire/Tube Ptir10 Ptir20 Ptir 25 Ptir30 for Medical Surgery

• Product Type: pipe
• Material: Platinum Iridium Alloy
• Carbon Content: -
• PCD: -
• ET: -
• Hole: -
• Model NO.: PtIr10
• Size: OD0.3*WT0.015mm Min.
• surface: Bright
• Name: Platinum Iridium tube
• Shape: PtIr pipe/wire
• MOQ: 200 Pcs
• sample: accepted small order
• applicaiton: medical components
• Transport Package: Wooden Case
• Specification: OD0.3*WT0.015mm Min.
• Trademark: TANKII
• Origin: Shanghai, China
• HS Code: 75052200
• Production Capacity: 10 Tons/Year

Product Description

PT90IR10 Pure Platinum Iridium tube shadow ring Ultra Fine Capillary Pipe  Alloy Tubes

Platinum Iridium alloy is a high -temperature metal. it consists of two metals: platinum and Iridium, which has excellent performance such as high strength, high corrosion resistance and high melting point. Widely used in the aerospace industry, medical equipment and other fields. The shadow ring is a marker ring used for X -ray development marks in the remote working area during interventional therapy, which belongs to disposable medical materials;High melting point, corrosion resistance, good cold processing performance, high accuracy; In line with human biocompatibility,stable transmission information, can be implanted; Product specifications:OD:0.3-5.0mm,wall thickness:0.015-0.2mm,support non-standard customization.Materials: Pt90lr10.

OD mm

W.T. /mm

≥0.015

≥0.02

≥0.05

≥0.10

≥0.20

≥0.30

≥0.40

≥0.50

≥0.60

≥0.70

≥0.80

≥0.90

≥1.00

≥1.5

≥0.3

-

-

-

≥0.5

-

-

-

-

-

≥1.0

-

-

-

-

-

-

-

≥1.5

-

-

-

-

-

-

-

-

-

≥2.0

-

-

-

-

-

-

-

-

-

≥3.0

-

-

-

-

-

-

-

-

-

-

≥4.0

-

-

-

-

-

-

-

-

-

-

-

≥5.0

-

-

-

-

-

-

-

-

-

-

-

-

≥6.0

-

-

-

-

-

-

-

-

-

-

-

-

-

≥7.0

-

-

-

-

-

-

-

-

-

-

-

-

-

≥8.0

-

-

-

-

-

-

-

-

-

-

-

-

≥9.0

-

-

-

-

-

-

-

-

-

-

-

≥10.0

-

-

-

-

-

-

-

-

-

-

≥15.0

-

-

-

-

-

-

-

-

-

≥20.0

-

-

-

-

-

-

-

-

 

Material	Melting point (ºC)	Density (G/cm3)	Vickers hardnes Soft	Vickers hardnes Hard	Tensile force (MPa)	Resistivity (uΩ.cm)20ºC
Platinum (99.99%)	1772	21.45	40	100	147	10.8
Pt-Rh5%	1830	20.7	70	160	225	17.5
Pt-Rh10%	1860	19.8	90	190	274	19.2
Pt-Rh20%	1905	18.8	100	220	480	20.8
Platinum-Ir (99.99%)	2410	22.42
Pure Platinum-Pt (99.99%)	1772	21.45
Pt-Ir5%	1790	21.49	90	140	174	19
Pt-lr10%	1800	21.53	130	230	382	24.5
Pt-Ir20%	1840	21.81	200	300	539	32
Pt-lr25%	1840	21.7	200	300	238	33
Pt-Ir30%	1860	22.15	210	300	242	32.5
Pt-Ni10%	1580	18.8	150	320	441	32
Pt-Ni20%	1450	16.73	220	400	588	34.1
Pt-w%	1850	21.3	200	360	588	62
Applications: Gas sensors. Various sensors, medical components. Electric and heating probes, etc.