Powder Metallurgy APM FECRAL Resistance Kan A-1 3.0mm Kan A1 APM Alloy 145 heating Wire for Cooking

• Customization: Available
• Product Type: Wire
• Material: APM
• Model NO.: APM
• PCD: -
• ET: -
• Hole: -
• Resistivity: 1.45
• MOT: 1420 C
• Density: 7.1 g/cm3
• sample: accept
• surface: Oxidation, bright
• Diameter: 0.02-10mm
• standard: GB
• Transport Package: Coil + Wooden Case
• Specification: 0.02-10.0mm
• Trademark: TANKII
• Origin: Shanghai, China
• HS Code: 72230000
• Production Capacity: 2000 Tons/Year

Product Description

TK-APM Ferro-Chromium-Aluminum Alloy
This product takes refined master alloy as raw material, uses powder metallurgy technology
to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat
treatment process. The product has the advantages of strong oxidation resistance, good
corrosion resistance at high temperature, small creep of electrothermal components, long service
life at high temperature and small change of resistance. It is suitable for high temperature 1420 C,
high power density, corrosive atmosphere, carbon atmosphere and other working environments.
It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces,
electronic industrial furnaces and diffusion furnaces.

main composition

	C	Si	Mn	Cr	Al	Fe
Min	-	-	-	20	5.5	Bal.
Max	0.04	0.5	0.4	22	6.0	Bal.

Main mechanical properties 
Tensile Strength at Room Temperature: 650-750MPa
 Elongation rate: 15-25%
hardness: HV220-260
1000ºCTensile Strength at 1000ºC Temperature 22-27MPa
1000ºC6MPa High Temperature Durability at 1000 Temperature and 6MPa ≥100h
 Main physical properties
density 7.1g/cm3
resistivity 1.45×10-6 Ω.m
Resistance Temperature Coefficient(Ct)
melting point:1500ºC
Maximum Continuous Working Temperature 1400ºC
 

800ºC	1000ºC	1400ºC
1.03	1.04	1.05

Average linear expansion coefficient()

20-800ºC	20-1000ºC	20-1400ºC
14	15	16

Fast life

	1300ºC	1350ºC
Average Fast Life (Hours)	110	90
Sagging rate after rupture	8	11