CuMn12Ni Manganese Copper resistance wire 6j13 6J12 6J8

• Customization: Available
• Classification: Light Metal
• Min Thickness: 0.01mm
• Model NO.: CuMn12Ni
• Resisivity: 0.47ppm
• Elongation Rate: 15(Min)
• Tensile Strength(Hard): 635MPa(Min)
• Sample: Small Order Accepted
• standard: GB/ASTM/JIS/BIS/DIN
• surface: bright
• Density: 8.4(g/cm3)
• MOQ: 20kilograms
• OEM: YES
• Transport Package: in Roll, in Woodencase Outside
• Specification: 0.01-3mm*0.3-600mm
• Trademark: Taknkii
• Origin: China
• HS Code: 7409400000
• Production Capacity: 50t/Month

Product Description

CuMn12Ni Manganese Copper resistance wire 6j13 6J12 6J8 
 
Product Description
Shunt Manganin widely used for Shunt resistor with the highest requirements, shunt manganin has been used in precision built electrical components such as Wheatstone bridges, decade boxes, voltage drivers, potentiometers and resistance standards.
 
 
Chemical Content, %

Ni	Mn	Fe	Si	Cu	Other	ROHS Directive
						Cd	Pb	Hg	Cr
2~5	11~13	<0.5	micro	Bal	-	ND	ND	ND	ND

 
 
Mechanical Properties

Max Continuous Service Temp	0-100ºC
Resisivity at 20ºC	0.44±0.04ohm mm2/m
Density	8.4 g/cm3
Thermal Conductivity	40 KJ/m·h·ºC
Temp Coefficient of Resistance at 20 ºC	0~40α×10-6/ºC
Melting Point	1450ºC
Tensile Strength(Hard)	585 Mpa(min)
Tensile Strength,N/mm2   Annealed,Soft	390-535
Elongation	6~15%
EMF vs Cu, μV/ºC (0~100ºC)	2(max)
Micrographic Structure	austenite
Magnetic Property	non
Hardness	200-260HB
Micrographic Structure	Ferrite
Magnetic Property	Magnetic

Product Description:
1 .Material:  6J13 manganin and pure copper (reach the GB614599 F2 standard)
2. Welding mode: Electric beam welding shunt. Braze welding with Ag-based alloy as solder.
3. Resistance value tolerance: ±5%
4. Shunt type: The shunt should be mountable type with holes for screw fixing
5. Termination: Integrated lead wires are available

6. Temperature: Independent from temperature variation with low TCR value,

7. Characteristics: TC < 50PPM/K

8. Aging: 10 hours under 120 deg.

9. Power loss: <50 mill watt

 

material:	iron,stainless steel,brass,bronze,carbon steel,aluminium alloy,spring steel,cold rolled steel etc.
process:	coating,stamping,cutting,bending,punching,welding,plating etc.
surface treatment:	nickel, zinc, Chrome, gold, tin, silver,printing,and colour zinc etc.
application:	mutual inductor,relay,thermostat,auto parts,furniture,transformer,computer and tableware etc.