High pressure resistance C17500 Copper sheet Bronze strip

• Customization: Available
• Product Type: copper Alloy
• Density: 8.4(g/cm3)
• Sample: Small Order Accepted
• surface: Bright
• colour: Bronze
• Elongation: 30%
• Other Name: CB101
• Transport Package: in Roll, in Woodencase Outside
• Specification: thick: 0.01-5mm, width: 1-600mm
• Trademark: TANKII
• Origin: Shanghai, China
• HS Code: 7409400000
• Production Capacity: 5000 Ton/Year

Product Description

High pressure resistance C17500 Copper sheet DIN2.1285

Unusual wear resistance 
High property levels 
High yield strength 
High hardness values
 
Beryllium Copper Chemical Composition
 

ASTM	Cu	Ni	Co	Be
C17200	Balance	1	1	1.80-2.10
C17000	Balance	1	1	1.60-1.85
C17300	Balance	1	1	1.85-2.10

 

ASTM	Cu	Ni	Co	Be
C17500	Balance	-	2.4-2.7	0.4-0.7
C17510	Balance	1.4-2.2	0.3	0.2-0.6

 
beryllium copper C17200
 
Cube2--C17200 (CDA 172) Beryllium Copper is the most commonly utilized Copper Beryllium alloy and is notable for its highest strength and hardness compared to commercial copper alloys. C17200 alloy contains appr. 2% of beryllium and achieves its ultimate tensile strength can exceed 200 ksi, while the hardness approaches Rockwell C45. Meanwhile, the electrical conductivity is a minimum of 22% IACS in the fully aged condition.C17200 also exhibits exceptional resistance to stress relaxation at elevated temperatures.
 
Chemical Composition
 

Element	Component
Be	1.85-2.10%
Co+Ni	0.20% Min
Co+Ni+Fe	0.60% Max.
Cu	Balance

 
Typical Physical Properties
 

Density (g/cm3)	8.36
Density before age hardening (g/cm3	8.25
Elastic Modulus (kg/mm2 (103))	13.40
Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C)	17 x 10-6
Thermal Conductivity (cal/(cm-s-°C))	0.25
Melting Range (°C)	870-980

 
Mechanical property:(before heat treatment)
 

status	Tensile strength (Kg/mm3)	Hardness (HV)	Conductivity ( IACS%)	Elongation (%)
H	70-85	210-240	22	2-8
1/2H	60-71	160-210	22	5-25
0	42-55	90-160	22	35-70

 
 Mechanical property:(after heat treatment)
 

status	Tensile strength (Kg/mm3)	Hardness (HV)	Conductivity (IACS%)	Elongation (%)
H	130-151	380-420	22	1-5
1/2H	126-147	370-410	22	2-7
0	112-135	350-339	22	3-11

 
Features 
 
1. High thermal conductivity
 2. High corrosion resistance, especially suitable for polyoxyethylene (PVC) products mold.
 3. High hardness, wear resistance and toughness, as inserts used with mould steel and aluminium can make the mold play a       highly efficient, prolong the service life.
 4. Polishing performance is good, can achieve high mirror surface precision and complicated shape design.
 5. Good tackiness resistance, easy to welding with other metal, easy to machining, there is no need additional heat treatment.