(6J13, 6J12, 6J8) Manganese Enameled Manganin 43 47 Wire for Shunt Resistor

• Customization: Available
• Certification: RoHS, ISO9001, ASTM, JIS, GB, EN
• Surface Treatment: Color Coated
• Model NO.: 6J13
• Alloy: Alloy
• standard: GB/ASTM/JIS/BIS/DIN
• surface: bright
• Sample: Free
• Classification: Precious Metal
• Dia.: 0.02min
• Color: RED/ Black/Green/Nature
• MOQ: 1KG
• Packing: Standard
• Transport Package: According to Client′s Requirement
• Specification: 0.01-10mm
• Trademark: TANKII
• Origin: China
• HS Code: 7409900000
• Production Capacity: 2000tons/Year

Product Description

Manganin Wire/ Shunt Resistor (6J13, 6J12, 6J8)
 
 Product Description
Manganin wire widely used for low voltage instrumentation with the highest requirements, the resistors should be carefully stabilised and the application temperature should not exceed +60 °C. Exceeding the maximum working temperature in air may result in a resistance drift generated by oxidizing. Thus, the long-term stability can be affected negatively.  As a result, the resistivity as well as the temperature coefficient of  the electric resistance may slightly change. It is also used as low cost replacement material for silver solder for hard metal mounting.
 
Chemical Content, %

Ni	Mn	Fe	Si	Cu	Other	ROHS Directive
						Cd	Pb	Hg	Cr
2~5	11~13	<0.5	micro	Bal	-	ND	ND	ND	ND

 
 Mechanical Properties

Max Continuous Service Temp	0-100ºC
Resisivity at 20ºC	0.44±0.04ohm mm2/m
Density	8.4 g/cm3
Thermal Conductivity	40 KJ/m·h·ºC
Temp Coefficient of Resistance at 20 ºC	0~40α×10-6/ºC
Melting Point	1450ºC
Tensile Strength(Hard)	585 Mpa(min)
Tensile Strength,N/mm2   Annealed,Soft	390-535
Elongation	6~15%
EMF vs Cu, μV/ºC (0~100ºC)	2(max)
Micrographic Structure	austenite
Magnetic Property	non
Hardness	200-260HB
Micrographic Structure	Ferrite
Magnetic Property	Magnetic

 
Manganin Applications:  
 
1;  It is used for making wire wound precision resistance
 2;  Resistance boxes
 3; Shunts for electrical measuring instruments
 
Manganin foil and wire is used in the manufacture of resistors, particularly ammeter shunts, because of its virtually zero temperature coefficient of resistance value and long term stability. Several Manganin resistors served as the legal standard for the ohm in the United States from 1901 to 1990. Manganin wire is also used as an electrical conductor in cryogenic systems, minimizing heat transfer between points which need electrical connections. 
Manganin is also used in gauges for studies of high-pressure shock waves (such as those generated from the detonation of explosives) because it has low strain sensitivity but high hydrostatic pressure sensitivity.

Type of Insulation

Insulation-enamelled Name	Thermal LevelºC (working time 2000h)	Code Name	GB Code	ANSI. TYPE
Polyurethane enamelled wire	130	UEW	QA	MW75C
Polyester enamelled wire	155	PEW	QZ	MW5C
Polyester-imide enamelled wire	180	EIW	QZY	MW30C
Polyester-imide and polyamide-imide double coated enameled wire	200	EIWH (DFWF)	QZY/XY	MW35C
Polyamide-imide enamelled wire	220	AIW	QXY	MW81C