CuCr1Zr C18200 Chromium Zirconium Copper Alloys

• Customization: Available
• Type: Copper Bars
• Material: Cucrzr Alloy
• Model NO.: C18200
• Shape: Round
• Alloy: Alloy
• Color: Red
• Standard: ASTM
• Softening temperature: 550ºC
• hardness: 75HRB
• elongation: 15%
• Thermal conductivity: 330
• Transport Package: Wooden
• Specification: negotiable
• Trademark: tankii
• Origin: China
• HS Code: 7408229000
• Production Capacity: 20tons/Month

Product Description

CuCr1Zr C18150 Chromium Zirconium Copper Alloys

Material:C18150,C18200,C15000
 
Feature:
High strength:Tensile strength> 450Mpa
High hardness:HRB70-86 HB120-165
High conductivity:Conductivity> 75%
High softening point:475-600°C
High wear resistant high heat-resisting
High anti-deformation ability
Long serving life
 
High-strength, high conductivity high softening point electrode alloy

Item		Characteristics	Application
ASTM	DIN	JIS	GB
C18150	CuCr1Zr	--	--	High strength(Rm:≥450Mpa,HRB:70-86), High conductivity(conductivity IACS%:75-83),heat wear resisting, distortion prevention	Widely used for automobile and spaceship stencil plate and contact welding stainless steel.Ideal electrode material for seal welder, high-voltage switch welding material and circuit breaker material, best high-strength, high conductivity and high melting-point material used for continuous crystallization device in metallurgical trade, and widely used for lead frame.
C15000	CuZr	--	QZr0.2
C18200	Cur1	--	--

 
Chemical composition:

Articles	Composition
GB/QB	DIN/ASTM/JIS	Cr	Zr	Total impurity	Cu
QCr0.5Zr0.15	C18150	0.5-1.5	0.05-0.25	<0.2	Bal.
QCr0.5	C18200	0.6-1.2	-	<0.2	Bal.
QZr0.2	C15000/C15100	-	0.1-0.2	<0.2	Bal.
QZr0.4	-	-	0.3-0.5	<0.2	Bal.

 
Mechanical performances:

Description	Alloy Grade	Temper	Tensile Strength           (Mpa)	Elongation(%)	Hardness
Chromium Bronze	C18200	TH04	>380	>10	75-80
			>475	>10	72-80
			>450	>8	65-75
Chromium-zirconium copper	C18150	TH04	>450	>10	75-85
			>400	>10	73-85
			>380	>12	65-83
Zirconium Copper	C15000/C15100	TH04	>450	>10	75-85
			>400	>10	73-85
			>380	>8	63-83