C17200 XHMB beryllium copper strip

• Customization: Available
• Type: Copper Strips
• Application: Air Condition or Refrigerator, Water Tube, Water Heater, Oil Cooler Pipe
• Model NO.: C17200
• Shape: Coil
• Alloy: Alloy
• Color: Green
• Standard: ASTM
• Density: 8.4(g/cm3)
• Sample: Small Order Accepted
• surface: Bright
• colour: Bronze
• Elongation: 30%
• Other Name: CB101
• Product Type: copper Alloy
• Transport Package: in Roll, in Woodencase Outside
• Specification: thick: 0.01-5mm, width: 1-600mm
• Trademark: TANKII
• Origin: Shanghai, China
• HS Code: 7409400000
• Production Capacity: 5000 Ton/Year

Product Description

C17200 XHMB beryllium copper strip
copper beryllium manufacturer
Unusual wear resistance 
High property levels 
High yield strength 
High hardness values
 
Beryllium Copper Chemical Composition
 

ASTM	Cu	Ni	Co	Be
C17200	Balance	0.1	0.1	1.80-2.10
C17000	Balance	1	1	1.60-1.85
C17300	Balance	1	1	1.85-2.10

 

ASTM	Cu	Ni	Co	Be
C17500	Balance	-	2.4-2.7	0.4-0.7
C17510	Balance	1.4-2.2	0.3	0.2-0.6

 
beryllium copper C17200
 
Cube2--C17200 (CDA 172) Beryllium Copper is the most commonly utilized Copper Beryllium alloy and is notable for its highest strength and hardness compared to commercial copper alloys. C17200 alloy contains appr. 2% of beryllium and achieves its ultimate tensile strength can exceed 200 ksi, while the hardness approaches Rockwell C45. Meanwhile, the electrical conductivity is a minimum of 22% IACS in the fully aged condition.C17200 also exhibits exceptional resistance to stress relaxation at elevated temperatures.
 
Chemical Composition
 

Element	Component
Be	1.85-2.10%
Co+Ni	0.20% Min
Co+Ni+Fe	0.60% Max.
Cu	Balance

 
Typical Physical Properties
 

Density (g/cm3)	8.36
Density before age hardening (g/cm3	8.25
Elastic Modulus (kg/mm2 (103))	13.40
Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C)	17 x 10-6
Thermal Conductivity (cal/(cm-s-°C))	0.25
Melting Range (°C)	870-980

 
Mechanical property (Before Hardening treatment) :
 

status	Tensile strength (Kg/mm3)	Hardness (HV)	Conductivity ( IACS%)	Elongation (%)
H	70-85	210-240	22	2-8
1/2H	60-71	160-210	22	5-25
0	42-55	90-160	22	35-70

 
 After Hardening treatment 
 

Tensile strength (Kg/mm3)	Hardness (HV)	Conductivity (IACS%)	Elongation (%)
1070-1210	330-390	≥17	≥4