0Cr13al4 Bright and Annealed Heating Wire
Chemical Content, %
| C |
P |
S |
Mn |
Si |
Cr |
Ni |
Al |
Fe |
Other |
| Max |
| 0.12 |
0.025 |
0.020 |
0.50 |
≤0.7 |
12.0~15.0 |
≤0.60 |
4.0~6.0 |
Balance |
- |
Mechanical Properties
Max Continuous Service Temperature:
Resisivity 20ºC:
Density:
Thermal Conductivity:
Coefficient of Thermal Expansion:
Melting Point:
Elongation:
Micrographic Structure:
Magnetic Property: |
950ºC
1.25ohm mm2/m
7.40g/cm3
52.7 KJ/m·h·ºC
15.4×10-6/ºC (20ºC~1000ºC)
1450ºC
Min 16%
Ferrite
magnetic |
Temperature Factor of Electrical Resistivity
| 20ºC |
100ºC |
200ºC |
300ºC |
400ºC |
500ºC |
600ºC |
| 1.000 |
1.005 |
1.014 |
1.028 |
1.044 |
1.064 |
1.090 |
| |
| 700ºC |
800ºC |
900ºC |
1000ºC |
1100ºC |
1200ºC |
1300ºC |
| 1.120 |
1.132 |
1.142 |
1.150 |
- |
- |
- |
Feature:
With long service life.Heating up fast.High thermal efficiency.Temperature uniformity. Can use vertically. When being used in the rated voltage,there is no volatile matter.It i the ne environmental protection electric heating wire.And an alternative to the costly nichrome wire.Can be customized according to customer requirements
Usage:
It is widely used in industrial furnace, household electrical appliances, infrared heater, etc.
The key properties:
1.The thickness of surface insulation resistance to oxidation layer: 5-15 μ m.
2. Insulation resistance: multimeter detection infinity.
3.The voltage-endurance of insulating single layer is greater than the alternating voltage 60 ν without breakdown.
4. The use of voltage: 6-380 ν.
5. Using temperature: Maximum1200 ºC
6. Service life: not less than 6000 hours.
7.Thermal shock performance: Electric heating element can withstand the cold and hot impact 600-6000 times without deformation.