0.05mm CuNi23 Resistance Copper Nickel Alloy Price Wire

• Product Type: Wire
• Material: copper nickel
• Carbon Content: Low Carbon
• PCD: 114.3mm
• ET: 45mm
• Hole: 4
• Model NO.: CuNi23
• Transport Package: Standard Packaging
• Specification: Cu Bal, Ni 23%, Mn0.5%
• Trademark: TANKII
• Origin: Shanghai
• Production Capacity: 200 Ton/Month

Product Description

CuNi23 Resistance low temperature coefficient copper nickel binary alloy for heating cable of automobile heating cushion


Introduction
CuNi23 resistance alloy is one of copper nickel binary alloys, having low temperature coefficient of resistance. It is applied to make rheostat, shunt, controller and other low voltage electrical components with a maximum operating temperature of 300°C. Due to its good heat coefficient, this alloy is widely used in low temperature heating cable of automobile heating cushion, railway snow melting, etc.

 

Due to high tensile strength and increased resistivity values, the copper nickel alloy wires are the first choice for applications as resistance wires. With the different nickel amount in this product range, the characteristics of the wire can be chosen according to your requirements. Copper nickel alloy wires are available as bare wire, or enamelled wire with any insulation and self-bonding enamel. Furthermore, litz wire made of enamelled copper nickel alloy wire are available.

CuNi23Mn is a copper-nickel alloy (CuNi alloy) with medium resistivity for medium-low temperature resistances. The alloy is suitable for use at temperatures up to 400°C (750°F)

CuNi23Mn is very malleable and has a good resistance to corrosion until temperatures of 400°C. Ideal applications areas are all types of resistances used at low temperature.


CuNi23Mn is typically used in heating cables, fuses, resistors and various types of controllers.


Physical Data


Density 8.9 g/cm3
Specific Heat 0.37(J/kg 20°C)
Electrical Resistivity 0.03×10-6ohm.m
Melting Point 1150°C
Maximum Operating Temperature 400°C
Coefficient of linear expansion (coeff 10-6/°C) 15.7 from 20 to 1000°C


Typical Mechanical Properties


Mechanical Properties CuNi23
Tensile Strength 350 Mpa
Elongation 25%






Main Mechanical Properties:

		Cu	CuNi2	CuNi6	CuNi10	CuNi23Mn	CuNi44
Tensile strength	[N/mm²]	220-300	260-360	270-370	300-390	500-550	560-680
Yield strength at 1% elongation	[N/mm²]	120-200	140-240	160-220	140-250	200-330	400-500
Bending proof performance	[%]	100			160	760
Resistance (IACS)	[%]	101	34	17	12	6	3
Conductivity	[S*m/mm²]	58.5	20.0	10.0	6.7	3.33	2.0
Resistivity	[Ohm*mm²/m]	0.0171	0.05	0.10	0.1493	0.30	0.50
Thermal coefficient of resistance	[1E-6/K]	3900-4300	1100-1600	500-900	350-400	150-200	-80 - +40
Solderability	[-]	good	good	good	good	good	no conventional soldering

 

main property type		Cuni1	CuNI2	CuNI6	CuNi8	CuNI10	CuNi14	CuNi19	CuNi23	CuNi30	CuNi34	CuNI44
main chemical composition	Ni	1	2	6	8	10	14.2	19	23	30	34	44
	MN	/	/	/	/	/	0.3	0.5	0.5	1.0	1.0	1.0
	CU	rest	rest	rest	rest	rest	rest	rest	rest	rest	rest	rest
max working temperature		/	200	220	250	250	300	300	300	350	350	400
density g/cm3		8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9
resistivity at 20 °c		0.03 ± 10%	0.05± 10%	0.10± 10%	0.12± 10%	0.15± 10%	0.20± 5%	0.25± 5%	0.30± 5%	0.35± 5%	0.40± 5%	0.49± 5%
temperature coefficient of resistance		<100	<120	<60	<57	<50	<38	<25	<16	<10	-0	<-6
tensile strength mpa		>210	>220	>250	>270	>290	>310	>340	>350	>400	>400	>420
elongation		>25	>25	>25	>25	>25	>25	>25	>25	>25	>25	>25
melting point °c		1085	1090	1095	1097	1100	1115	1135	1150	1170	1180	1280
coefficient of conductivity		145	130	92	75	59	48	38	33	27	25	23