| Customization: | Available |
|---|---|
| Transport Package: | Standard Packing |
| Specification: | negotiable |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
|
Grade
|
Highest temperature
|
Resistivity
|
Hardness
|
Tensile strength
|
Elongation
|
|
0Cr13Al4
|
1050ºC
|
1.25±0.05μΩ.m
|
180-210HV
|
≥550N/mm2
|
≥16
|
|
0Cr15Al5
|
1100ºC
|
1.3±0.05μΩ.m
|
180-210HV
|
≥550N/mm2
|
≥16
|
|
0Cr21Al6Nb
|
1300ºC
|
1.42±0.05μΩ.m
|
200-240HV
|
750N/mm2
|
≥12
|
|
Cr20Ni80
|
1200ºC
|
1.09±0.05μΩ.m
|
180-220HV
|
750N/mm2
|
≥20
|
|
Cr15Ni60
|
1150ºC
|
1.12±0.05μΩ.m
|
175-210HV
|
750N/mm2
|
≥20
|
|
Cr20Ni35
|
1100ºC
|
1.04±0.05μΩ.m
|
180-220HV
|
750N/mm2
|
≥20
|
|
Cr25Ni20(310S)
|
1100ºC
|
0.86±0.05μΩ.m
|
180-220HV
|
750N/mm2
|
≥20
|
|
Grade
|
Chemical composition%
|
||||||||
|
C
|
P
|
S
|
Mn
|
Si
|
Cr
|
Ni
|
Al
|
Fe
|
|
|
≤
|
|||||||||
|
0Cr15Al5
|
0.04
|
0.02
|
0.01
|
0.3
|
≤0.5
|
13-14
|
<1
|
4.8-5.0
|
balance
|
|
0Cr21Al6Nb
|
0.05
|
0.025
|
0.02
|
0.5
|
≤0.6
|
21-23
|
≤0.6
|
5-7
|
balance
|
|
0Cr13Al4
|
0.04
|
0.02
|
0.01
|
0.3
|
≤0.5
|
13-14
|
<1
|
4.8-5.0
|
balance
|
|
Cr20Ni80
|
0.08
|
0.02
|
0.015
|
0.6
|
0.75-1.6
|
20-23
|
balance
|
<0.5
|
≤1.0
|
|
Cr15Ni60
|
0.08
|
0.02
|
0.015
|
0.6
|
0.75-1.6
|
15-18
|
55-61
|
<0.5
|
balance
|
|
Cr20Ni35
|
0.08
|
0.02
|
0.015
|
1.0
|
1-3
|
18-21
|
34-37
|
-
|
balance
|
|
Cr25Ni20
|
0.08
|
0.045
|
0.03
|
2.0
|
0.4-0.6
|
24-26
|
19-22
|
-
|
balance
|
|
Grade
|
Cr15Ni60
|
|
Size
|
thickness:0.05-3mm
width:4-250mm
|
|
Surface
|
bright slitting
|
|
Weight
|
5-200kg/roll ,according customers' quantity
|
|
Resistivity
|
1.12±0.05μΩ.m
|
|
Hardness(HV)
|
175-210HV
|
|
Elongation
|
≥20%
|