Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip

Product Details
Customization: Available
Product Type: Strip
Material: FeMn
Diamond Member Since 2008

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

Management System Certification
ISO 9001, ISO 14001
  • Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip
  • Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip
  • Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip
  • Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip
Find Similar Products

Basic Info.

Model NO.
C75200
Carbon Content
Low Carbon
PCD
100mm
ET
15mm
Hole
5
Size
T:0.01-5mm
surface
bright
standard
GB/ASTM/JIS/BIS/DIN
Sample
Small Oreder Accepted
Density
8.9(g/cm3)
state
Soft 1/4hard 1/2hard hard T-hard
Transport Package
500m/Spool
Specification
0.01-3mm*0.3-600mm
Trademark
TANKII
Origin
Shanghai, China
HS Code
7409400000
Production Capacity
3000ton/Year

Product Description

Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip

Product Description

Categories: High precision copper alloy strip & plate

Name: High performance zinc copper nickel alloy strip & plate

Number: C75200

Feature: Elasticity modulus: 115GPa

Good fatigue resistance.

Good electroplate performance

Welding performance is good

Fastness in high temperature

Good cold working, deep drawing, curve performance.

 Articles,Chemical composition

Articles Chemical composition
GB UNS EN JIS Cu% Ni% Zn%
BZn18-26 C77000 CuNi18Zn27 C7701 54-58 16.5-19.5 Rem

Physical properties,fabrication properties

Physical properties fabrication properties
density g/cm3 electrical conductivity %IACS thermal conductivity W/(m.K) modulus of elasticity GPa specific heat J/(g.K) cold-work
ability
machin
ability
electric plating property hot dip tin plating property weld
ability
8.7 5 32 125 0.34 excellent suitable excellent excellent good

Mechanical properties

Mechanical properties
State Hardness HV Tension test bending(in rolling direction)rest bending(transverse to rolling 
 THS
mm
tensile strength MPa yield strength MPa elongation
%
THs mm angles ID/THS THS angles ID/THS
1/2H 150-210 0.1-0.7 540-655 ≥390 ≥8 ≤1.6 180° 150%  ≤0.5 180° 300% 
≥0.71 540-655 ≥390 ≥11
H 180-240 0.1-0.7 630-735 ≥390 ≥500 ≥4 ≤1.6 180° 200%  ≤0.5 180° 400% 
≥0.71 630-735 ≥500 ≥6
EH 210-260 ≥0.1 705-805 ≥600 - ≤1.6 90° 300%  ≤0.5 90° 600% 
SH 230-270 ≥0.1 765-865 ≥680 - - - - - - -

Articles,Chemical composition

Articles Chemical composition
GB UNS EN JIS Cu% Ni% Zn%
BZn18-18 C75200 CuNi18Zn20 C7521 62-66 16.5-19.5 Rem

Physical properties,fabrication properties

Physical properties fabrication properties
density g/cm3 electrical conductivity %IACS thermal conductivity W/(m.K) modulus of elasticity GPa specific heat J/(g.K) cold-workability machinability electric plating property hot dip tin plating property
8.73 6 32 125 0.34 excellent suitable excellent excellent

Mechanical properties

Mechanical properties
State Hardness HV Tension test bending test
Thickness mm Tensile strength MPa elongation % thickness angles ID
0 - 0.1-5.0 ≥375 ≥20 ≤1.6 180° sticking closely
1/2H 120-180 0.1-5.0 440-570   ≥5   ≤1.6 180° 100% of thickness
≤0.5 200% of thickness
H 150-210

0.1-0.15

540-640  - ≤1.6 180° 200% of thickness
>0.15-5.0 ≥3 ≤0.5 400% of thickness
EH ≥185 0.1-5.0 ≥610 - - - -

Articles,Chemical composition

Articles Chemical composition
GB UNS EN JIS Cu% Ni% Zn%
BZn15-20 C75400 CuNi15Zn20 C7541 60-64 12.5-15.5 Rem

Physical properties,fabrication properties

Physical properties fabrication properties
density g/cm3 electrical conductivity %IACS thermal conductivity W/(m.K) modulus of elasticity GPa specific heat J/(g.K) cold-workability machinability electric plating property hot dip tin plating property
8.7 6 32 135 0.34 excellent suitable excellent excellent

Mechanical properties

Mechanical properties
State Hardness HV Tension test bending test
Thickness mm Tensile strength MPa elongation % thickness angles ID
0 - 0.1-5.0 ≥355 ≥20 ≤1.6 180° sticking closely
1/2H 110-170 0.1-5.0 410-540 ≥5 ≤1.6 180° 100% of thickness
H ≥135 0.1-0.15 ≥490 - ≤1.6   180° 200% of thickness
>0.15-5.0 ≥490 ≥3

Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip
Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip
Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip
Uns C75200 Copper-Nickel-Zinc Alloy Electrum Strip