NiFe30 nickel iron alloy wire RESISTHERM Alloy 30/NiFe52/NiFe55/NiFe60

• Customization: Available
• Product Type: Wire
• Material: Feni
• Model NO.: NiFe30
• PCD: -
• ET: -
• Hole: -
• Size: 0.01-10mm
• standard: GB/ASTM/JIS/BIS/DIN
• surface: bright
• Transport Package: Waterproof Paper, Wooden Case
• Specification: 0.3mm--10mm
• Trademark: TANKII
• Origin: China
• HS Code: 7505220000
• Production Capacity: 300tons/Month

Product Description

NiFe30 nickel iron alloy wire RESISTHERM Alloy 30/NiFe52/NiFe55/NiFe60

material: NiFe52, NiFe28, NiFe30
stable resistance
straight and solid spooling
long life service
 
Ferro nickel alloy includes: FeNi30,FeNi36, FeNi36, Permalloy ((1J79,  1J86,  1J85), 4J29(Kover), 79Ni4MoFe, 80Ni5MoFe, 1J50 (Ni50)
 
FeNi
Nifethal 52 is a nickel-iron alloy (NiFe alloy) for use at temperatures up to 600°C (1110°F). The alloy is characterized by low resistivity and high temperature coefficient of resistance.
 Typical applications for Nifethal 52 are in voltage regulators, timing devices, temperature sensitive resistors, temperature compensating devices, and low temperature heating applications.
 

Alloy Designation	C	P	S	Mn	Si	Cu	Ni	Fe
NiFe52	≤0.05	≤0.02	≤0.02	≤0.6	≤0.8	-	50.5~52.5	Remain
NIFe55	≤0.1	≤0.02	≤0.02	≤0.4	≤0.5	-	54.0~56.0	Remain
NiFe60	≤0.1	≤0.02	≤0.02	≤0.8	≤0.5	≤0.2	57.0~60.0	Remain

NiFe30 Chemical composition

	Ni %	Fe %
Nominal composition	Bal.	30

Mechanical properties

Wire size	Yield strength	Tensile strength	Elongation
Ø	Rp0.2	Rm	A
mm	MPa	MPa	%
0.5	340	600	30

Physical properties

Density g/cm3	8.50
Electrical resistivity at 20°C Ω mm2/m	0.33

 

Temperature factor of resistivity
Temperature °C	100	150	200	250	300	350	400	450	500
resistivity	0.41	-	0.52	-	0.64	-	0.76	-	0.89

 

Coefficient of thermal expansion
Temperature °C	Thermal Expansion X10-6/K-1
20-100	25

 

Thermal conductivity
Temperature °C	20
W m-1 K-1	25

 

Specific heat capacity
Temperature °C	20
kJ kg-1 K-1	0.42

 

Melting point °C	1400
Max continuous operating temperature in air °C	600
Magnetic properties	The material is magnetic up to approximately 530°C (the Curie point).