Manufactory Price 1Cr13Al4 Fecral Alloy Wire with High Resistance

• Customization: Available
• The highest temperature: 1250ºC
• Melting point: 1500ºC
• density: 7.1G/M³
• hardness: 200~260HB
• Transport Package: Waterproof Paper, Wooden Case
• Specification: 0.1mm-30mm
• Trademark: TANKII
• Origin: Shanghai, China
• HS Code: 7408229000
• Production Capacity: 200 Ton/Month

Product Description

Manufactory Price 1Cr13Al4 Fecral Alloy  Wire with High Resistance and Electrical Heating Alloy
 

Chemical Content, %

C	P		S	Mn	Si	Cr	Ni	Al	Fe	Other
Max
0.12		0.025	0.020	0.50	≤0.7	12.0~15.0	≤0.60	4.0~6.0	Balance	-

 
Mechanical Properties

Max Continuous Service Temperature: Resisivity 20ºC: Density: Thermal Conductivity: Coefficient of Thermal Expansion: Melting Point: Elongation: Micrographic Structure: Magnetic Property:

950ºC 1.25ohm mm2/m 7.40g/cm3 52.7 KJ/m·h·ºC 15.4×10-6/ºC (20ºC~1000ºC) 1450ºC Min 16% Ferrite magnetic

 
Temperature Factor of Electrical Resistivity

20ºC	100ºC	200ºC	300ºC	400ºC	500ºC	600ºC
1.000	1.005	1.014	1.028	1.044	1.064	1.090
700ºC	800ºC	900ºC	1000ºC	1100ºC	1200ºC	1300ºC
1.120	1.132	1.142	1.150	-	-	-

Feature:
With long service life.Heating up fast.High thermal efficiency.Temperature uniformity. Can use vertically. When being used in the rated voltage,there is no volatile matter.It i the ne environmental protection electric heating wire.And an alternative to the costly nichrome wire.Can be customized according to customer requirements

Usage:
It is widely used in industrial furnace, household electrical appliances, infrared heater, etc.
The key properties:
1.The thickness of surface insulation resistance to oxidation layer: 5-15 μ m.
2. Insulation resistance: multimeter detection infinity.
3.The voltage-endurance of insulating single layer is greater than the alternating voltage 60 ν without breakdown.
4. The use of voltage: 6-380 ν.
5. Using temperature: Maximum1200 ºC
6. Service life: not less than 6000 hours.
7.Thermal shock performance: Electric heating element can withstand the cold and hot impact 600-6000 times without deformation.