0Cr15Al5 FeCrAl Alloy Electric Resistance Wire for Industrial Heating Furnace

• Customization: Available
• Type: Bare
• Conductor Type: Solid
• Model NO.: 0Cr15Al5
• Conductor Material: Alloy
• Sheath Material: N/A
• Insulation Material: Bare
• Material Shape: Flat Wire
• Range of Application: Heating element
• Certification: ISO9001, RoHS
• Brand: N/A
• Shipping Method: By air/sea, by FedEx, by UPS
• Surface: bright, annealed, soft
• Size: As customer required
• Packing: spool, coil, carton, plywood case
• Feature: Heat resistant, corrosion resistant, weldability
• Usage: Furnace, glass top hob, hetaing blanket
• Chemical Composition: Iron Chromium Aluminium
• Free Sample: Available
• Shape: wire/flat wire/ribbon/strip
• Condition: soft, half hard, hard
• Color: Bright
• Advantage: High using temperature
• Resistivity: 1.25
• Density: 8.4
• Appearance: Bright smooth
• Transport Package: Spool, Carton, Wooden Case
• Specification: Rohs
• Trademark: TANKII
• Origin: China
• HS Code: 72230000
• Production Capacity: 5000 Annually

Product Description

0Cr15Al5 FeCrAl Alloy Heat Resistance Wire for Industrial Heating Furnace 

Resistance wire is usually used in resistor. Our resistance have small tolerance on size and electrical resistance value

1) Material available:

Cr20Ni80, Cr30Ni70, Cr15Ni60, Cr20Ni35, Cr20Ni30, Cr20Ni25, NiCr25FeAlY, Cr13Al4, Cr21Al4, Cr14Al4, Cr20Al4, Cr21Al6, Cr23Al5, Cr25Al5, Cr21Al6Nb, Cr25Al5SE.


2) Shape:

Wire, strip, ribbon, sheet, coil


3) About us:

We can also design and manufacture according to your request. Shanghai Tankii Alloy Material Co., Ltd. is specialized in production of Ni-Cr Alloy, Cu-Ni Alloy, Fechral, thermocouple wire, pure nickel and other precision alloy materials in the form of wire, strip, rod, bar and plate.

4) Alloy character:

Ferritic alloys allow to reach process temperatures of 2192 to 2282F,
Corresponding to a resistance temperature of 2372F. All ferritic alloys have approximatively the same basis composition: 20 to 25 % of chromium, 4.5 to 6 % of aluminium, balance being iron. Some of them contain in addition rare earth, as yttrium or silicium. Those alloys having a ferritic structure, we observe, after a maintenance at high operating temperature, an important growth of the grain and a precipitation of chromium carbides at the grain joints level. This induces an increased embrittlement of the resistance, especially when it is come again at ambient temperature.

Specification:

Alloy Type	Diameter	Resistivity	Tensile	Elongation (%)	Bending	Max. Continuous	Working  Life
	(mm)	(μΩm)(20°C)	Strength		Times	Service	(hours)
			(N/mm²)			Temperature (°C)
Cr20Ni80	<0.50	1.09±0.05	850-950	>20	>9	1200	>20000
	0.50-3.0	1.13±0.05	850-950	>20	>9	1200	>20000
	>3.0	1.14±0.05	850-950	>20	>9	1200	>20000
Cr30Ni70	<0.50	1.18±0.05	850-950	>20	>9	1250	>20000
	≥0.50	1.20±0.05	850-950	>20	>9	1250	>20000
Cr15Ni60	<0.50	1.12±0.05	850-950	>20	>9	1125	>20000
	≥0.50	1.15±0.05	850-950	>20	>9	1125	>20000
Cr20Ni35	<0.50	1.04±0.05	850-950	>20	>9	1100	>18000
	≥0.50	1.06±0.05	850-950	>20	>9	1100	>18000
1Cr13Al4	0.03-12.0	1.25±0.08	588-735	>16	>6	950	>10000
0Cr15Al5		1.25±0.08	588-735	>16	>6	1000	>10000
0Cr25Al5		1.42±0.07	634-784	>12	>5	1300	>8000
0Cr23Al5		1.35±0.06	634-784	>12	>5	1250	>8000
0Cr21Al6		1.42±0.07	634-784	>12	>5	1300	>8000
1Cr20Al3		1.23±0.06	634-784	>12	>5	1100	>8000
0Cr21Al6Nb		1.45±0.07	634-784	>12	>5	1350	>8000
0Cr27Al7Mo2	0.03-12.0	1.53±0.07	686-784	>12	>5	1400	>8000