Soft Magnetic Alloys Wire 1J54 / FeNi 54 / Ni50Cr14Si

• Customization: Available
• Product Type: Wire
• Material: Feni
• Model NO.: SMTK 54-W
• Carbon Content: Low Carbon
• Surface: Bright
• Condition: Soft / Hard
• Package: Wooden Case
• Certificate: Magnetic( Permeability and Magnetic Induction)
• Diameter: 0.1~10mm
• Transport Package: Wooden Case
• Trademark: SMTK 54-W
• Origin: China
• HS Code: 750522000
• Production Capacity: 3000 Tons/Year

Product Description

Soft Magnetic Alloys Wire 1J54 / FeNi 54 / Ni50Cr14Si

Mainly used  in two areas for energy conversion and information processing.

In the power industry, mainly in the high magnetic field has a high magnetic induction and low core loss of the alloy. In the electronics industry, mainly at low or medium alloy having a high magnetic permeability and low coercive force. At high frequencies shall be made on a thin strip or alloy higher resistivity. Usually with sheet or strip.

Soft magnetic materials in exchange for use, due to the alternating magnetic eddy currents are induced inside the material, resulting in the loss, the smaller the resistance of the alloy, the greater the thickness, the higher the frequency of the alternating magnetic field, eddy current losses greater, magnetic reduce more. For this, the material must be made thinner sheet (tape), and the surface coated with an insulating layer, or the use of certain methods to the surface to form an oxide insulating layer, such alloys commonly used magnesium oxide electrophoresis coating.

Iron-nickel alloy mostly in the alternating magnetic field use, mainly for yoke iron, relay, Small Power Transformers and Magnetically shielded.

Chemical composition

composition	C	P	S	Cu	Mn
	≤
Content(%)	0.30	0.020	0.020	0.20	0.30~0.60

 

composition	Si	Ni	Cr	Fe
Content(%)	1.10~1.40	49.0~51.0	3.80~4.20	Bal

Physical properties

Shop sign	Linear expansion coefficient	Resistivity (μΩ·m)	Density (g/cm³)	Curie point (ºC)	Saturation magnetostriction coefficient  (10-6)
1j54	—	0.90	8.2	360	—

Heat treatment system

shop sign	Annealing medium	heating temperature	Keep the temperature time/h	Cooling rate
1j50	Dry hydrogen or vacuum, pressure is not greater than 0.1 Pa	Along with the furnace heating up 1100~1150ºC	3~6	In ≤200 ºC / h speed cooling to 400~500 ºC, fast to 200 ºC draw a charge